Rust in stainless steel and high-temperature alloy steel processing application. During roughing, the choice of 3% to 5% of the emulsion or 10% to 15% of the extreme pressure emulsion, extreme pressure cutting oil and curing oil. When finished, use extreme pressure cutting oil, or 10% to 20% of the extreme pressure emulsion, oil curing, curing oil 80% ~ 85% + CCl4 15% ~ 20%, mineral oil + 78% to 80% of black oil or rust and lard 18% + 1.7% sulfur, machine oil 90% + CCl4 10%, kerosene 50% oleic acid, 25% + 25% + vegetable oil. Broaching, tapping and reaming, with 15% to 20% of rust or extreme pressure cutting oil, soybean oil or vegetable oil sulfide; add oil in the curing power outlet CCl4 10% ~ 20%, adding 20 in lard % ~ 30% CCl4, and 10% to 15% of kerosene used in sulfurized oil reaming. Sulfurized oil was added in 1.5% ~ 20% CCl4 or mechanical self lead oil plus oil, chlorinated paraffin or diluted with kerosene, or MoS2 ointment for tapping. When hobbing and slotting should be 20% to 25% using extreme pressure cutting oil emulsion or extreme pressure. When drilling, with 10% to 15% emulsion or a 10% to 15% of a rust inhibitor, extreme pressure cutting oils. High-temperature alloys. In addition to the use of cutting fluid with an outer stainless steel, roughing, with potassium nitrite, potassium 2% + 1% + 7% + triethanolamine 7% to 10% glycerol + water balance or sebacic acid 7% ~ 10 % + 5% + sodium nitrite triethanolamine 7% to 10% + 7% rust inhibitor to 10% + 7% to 10% glycerol + water balance. For nickel-based superalloy, you should avoid using sulfur cutting fluid to avoid stress corrosion, the part of the fatigue strength. Application Guide rust rust inhibitor is a non-barium, lead, silver, mercury and other heavy metal ions in aqueous solution of copper-based anti-rust rust inhibitor, can effectively protect the steel, iron and other materials, rust inhibitor, to prevent rust . Depending on the requirements of rust and water at a certain ratio mix plant rust, rust period up to a few days to a few months, if there are certain conditions for packaging, rust time of up to one year. Recommended processing turning the grinding process directly with rust inhibitor diluted watered ratio of 1: 20-50 times, with good cooling, lubrication, cleaning, rust-proof function, or directly using the company THIF-111 water-based cutting fluid rust-proof aluminum agents, such machined workpiece clean good cleaning, and small surface rust. Water-based cleaning agent again workpiece machining process to remove the dirt attached to the surface, it is recommended to use rust THIF-301 water-based cleaning agent. According to anti-rust deadlines, please refer to the following ratio and methods: Use the rust can meet the requirements of short-term rust. After the operation, then the workpiece on the rust inhibitor 1: 15-20 fold dilution in water to soak for 1-2 minutes, at room temperature for 3-6 months may rust. , After the operation, and then put the rust of the workpiece 1: 5-10-fold diluted with water to soak for 1-2 minutes, then packed in plastic bags, plus cartons, can be more than one year anti-rust, for brakes, hub , auto parts, hardware and exports, inventory and other rust. Please bring latex gloves to prevent perspiration, rust better. Steel rust, Dongguan Ferrer trade, enterprises stone rust provided by the Dongguan City Ferrer Trading Limited. Trade Co., Ltd. of Dongguan City Ferrer (www.furui-china.com) is Dongguan, industrial cleaners leaders, over the years, the company is implementing the scientific management, innovation and development, the principle of honesty and trustworthiness, and satisfy customer needs . Ferrer trade in Dongguan leadership with the staff warmly welcome all inquiries negotiations to create Dongguan Ferrer trade a better future.